Preparation and Characterization Of Co3O4 Nano Powder
Synthesis of Co3O4 has been done using Co(NH3)4.6H2O and KOH as precursors with molar ratio 1:1 M with precipitation method. Several of calcination temperature were done to learn type of mineral phase and crystalinity of Co3O4 synthesized. The XRD analysis revealed that calcination temperature influence crystalinity and mineral phase of Co3O4 prepared and calcination temperature at 700 oC has highest intensity and crystalinity that others. Analysis of particle size was examined using Schererr equation, and the results showed that particle size decrease with calcination temperature. The particle size at 700 oC was = 32.387 nm. Analysis morphology of Co3O4 was examinedusing SEM technique, and the result revelaed Co3O4 have nearly spherical.
Allaedini G. Tasirin SM, Pudukudy M. 2014. Effect of pH on cobalt oxide nanoparticles prepared by co-precipitation method. Australian Journal Of basic and Applied Sciences. 8(19): 243-247.
Binita NN, Suraja PV, Yakoob Z, Resmi MR, Silija PP. 2010. Simple synthesis of Co3O4 nanoflake using low temperature sol-gel method suitable for degradation od dyes. J.Sol-gel.Sci-Techno. 53: 466-469.
Che Z, Chen S, Li Y, Si X, Huang J, Massey S, Chen S. 2014. A recyclable and highly active Co3O4 nanoparticles/titanate nanowire catalyst for organic dyes degradation with peroxymonosulfate. Materials Research Bulletin. 57: 170–176.
Chen Z, Xu A, Zhang Y, Gu N. 2013. Corrigendum to preparation of NiO and CoO nanoparticles using M2þ-oleate (M ¼ Ni, Co) as precursor. Current Applied Physics. 13: 307.
Ezema F, Ezugwu S, Agbo S, Ekwealor A, Asogwa P, Osuji R. 2009. 24th European Photovoltaic Solar Energy Conference, Hamburg.
Feng, Zeng. 2003.Size-controlled growth of Co3O4 Nanocubes. Chemistry of Materials. 15(14): 2829–2835. kotabunga
Goudarzi M, Bazarganipour M, Niasari MS. 2014. Synthesis, characterization and degradation of organic dye over Co3O4 nanoparticles prepared from new binuclear complex precursors. RSC Adv. 4: 46517–46520.
Gu Y, Jian F, Wang X. 2008. Synthesis and characterization of nanostructured Co3O4 fibers used as anode materials for lithium ion batteries Thin Solid Films. 517: 652–655.
Lai TL, Lai YL, Lee CC, Shu YY, Wang CB. 2008. Microwave-assisted rapid fabrication of Co3O4 nanorods and application to the degradation of phenol. Catal. Today. 131: 105.
Manigandan R, Giribabu K, Suresh R, Vijayalakshmi L, Stephen A, Narayanan V. 2013. Cobalt oxide nanoparticle: charactization and its electrocatalytic activity toward Nitrobenzene. Chemical Science Transaction. 2: S47-S50.
Nassar MY, Ahmed IS. 2012. Template-free hydrothermal derived cobalt oxide nanopowders: Synthesis, characterization, and removal of organic dyes. Materials Research Bulletin. 47: 2638–2645.
Ressler T, Walter A, Scholz J, Tessonnier JP, Su DS. 2010 Structure and properties of a Mo oxide catalyst supported on hollow carbon nanofibers in selective propene oxidation. Journal of Catalysis. 271: 305–314.
Sadiq MMJ, Nesaraj AS. 2014. Reflux condensation synthesis and characterization of Co3O4 nanoparticles for photocatalytic applications. Iranian Journal Of Catalisys. 4(4): 219-226.
Sharifi S, Shakur H, Mirzaei A, Salmani A, Hosseini M. 2013. Characterization of cobalt oxide Co3O4 nanoparticles prepared by various methods: Effect of calcination temperatures on size, dimension and catalytic decomposition of hydrogen peroxide. Int. J. Nanosci. Nanotechnol. 9(1): 51-58.
Sinkó K, Szabó G, Zrínyi M. 2011. Liquid-Phase Synthesis of Cobalt Oxide Nanoparticles. Journal of Nanoscience and Nanotechnology. 11: 1–9.
- There are currently no refbacks.
Copyright (c) 2019 Pepi Helza Yanti, Akmal Mukhtar, . Astarina
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.