Analisis Nilai Fraksi β Dari Film Tipis Polimer Komposit PVDF/Fe3O4 Terhadap Konsentrasi Fe3O4
Abstract
Abstrak
Film tipis telah dibuat dengan mengompositkan PVDF yang berperan sebagai matriks dan Fe3O4 yang menjadi pengisi dengan menggunakan metode celup sederhana. Penelitian ini dilakukan dengan pengujian XRD setiap sampel dengan 4 variasi konsentrasi 2%, 4%, dan 6% dari Fe3O4 untuk diketahui pengaruh konsentrasi Fe3O4 terhadap nilai fraksi
Keywords
Full Text:
PDFReferences
A. Hartono, S. Satira, M. Djamal, R. Ramli, H. Bahar, and E. Sanjaya, “Effect of Mechanical Treatment Temperature on Electrical Properties and Crystallite Size of PVDF Film,” Adv. Mater. Phys. Chem, vol. 3, 2013, pp. 71–76, 2013.
A. Hartono, S. Satira, M. Djamal, and E. Sanjaya, “Poly ( vinylidene fluoride) Thin Film Prepared by Roll Hot Press,” Adv. Mater. Phys. Chem, vol. 3, no. 1, pp. 7–11, 2013.
L. Andrew, “Poly-(vinylidene Fluoride),” New Jersey, Bell Lab, 1981.
A. Hartono, S. Satira, and M. Djamal, “Characterization Analysis of PVDF Thin Films Fabricated Using Deep Coating Machines,” Adv. Mater. Phys. Chem, vol. 149, pp. 129–132, 2018.
J. M. H. and J. Spalek, “Electronic properties of NiS2−? Se? single crystals: from magnetic mott−hubbard insulators to normal metals,” Chem. of Materials, vol. 10, no. 10, pp. 2910–2929, 1998.
K. C. N. R. Rao, S. R. C. Vivekchand, “Synthesis of inorganic nanomaterials,” Dalt. Trans., no. 34, pp. 3728–3749, 2007.
M. Z. and G. Diao, “Synthesis of porous Fe3O4 nanospheres and its application for the catalytic degradation of xylenol orange,” J. Phys. Chem. C, vol. 115, no. 39, pp. 18923–18934, 2011.
T. Prabhakaran and J. Hemalatha, “Ferroelectric and magnetic studies on unpoled Poly ( vinylidine Fluoride )/ Fe3O4 magnetoelectric nanocomposite structures,” Mater. Chem. Phys., vol. 137, no. 3, pp. 781–787, 2013.
Claassen A A, “Proceedings of the Physical Society", London, no. 38. p. 482-487. 1926.
R.Hasegawa, Y.Takahashi, Y.Chatani, H.Tadokoro, Polymer Journal, Tokyo, no. 3, p. 600. 1972
DOI: https://doi.org/10.15408/fiziya.v3i1.15020 Abstract - 0 PDF - 0
Refbacks
- There are currently no refbacks.
This work is licensed under a CC-BY-SAÂ